Ni_0.7-xZn_0.3M_xFe₂O₄ (M=Mn²⁺, Co²⁺, and Cu²⁺; x=0.0, 0.1, 0.3, 0.5, and 0.7) spinel-type ferrite were fabricated through citrate technique. The X-ray diffraction analysis disclosed the creation of the cubic phase spinel structure in all prepared samples, except for the high concentration of Mn (x=0.7). As the concentration of dopant ions increased, the structural parameters, such as lattice constant, particle size, X-ray density, bulk density, and percentage porosity showed interesting changes. The experimental lattice parameter was found in the range from 0.839 to 0.843 nm for the three investigated series. The average particle size ranged from 52 to 107 nm. The density decreased with the addition of Mn and Co, while it improved considerably with the increment of Cu content. Besides, the percentage porosity for Ni-Zn-Cu ferrite was lower than those for the Ni-Zn-Mn and Ni-Zn-Co ferrite series. Several magnetic properties were studied at room temperature. Magnetization curves were measured in the range of magnetizing field up to 6000 Am^-1. The magnetization was studied at a constant magnetic field (4500 Am^-1) and it was found to rise with Mn²⁺ ions content up to x=0.3 followed by a subsequent decline at x=0.5. Furthermore, a monotonic decrease in the magnetization was observed by the incorporation of Co into Ni-Zn ferrite, while an increase was noticed for Cu-substituted samples. Among the three investigated series, the Ni-Zn-Cu ferrite series exhibited the highest magnetization, making it appropriate for high-density recording media. The initial permeability (μ_i) was studied as a function of temperature for all samples. The Curie temperature T_C was estimated from the μ_i(T) plot and was determined to decrease with the upsurge in the content of substitute ions (Mn²⁺, Co²⁺, and Cu²⁺). Keywords: spinels, citrate method, SEM, magnetic properties.

Подсчитывается количество просмотров абстрактов ("html" на диаграммах) и полных версий статей ("pdf"). Просмотры с одинаковых IP-адресов засчитываются, если происходят с интервалом не менее 2-х часов.

Дата начала обработки статистических данных - 27 января 2016 г.